Polyester-based Thermoplastic Polyurethane
Properties | Key | NORM | Value | Unit |
---|---|---|---|---|
Hardness (after 3 sec.) | M | ASTM D 2240 | 73 | Shore A |
Hardness (after 3 sec.) | M | ASTM D 2240 | 25 | Shore D |
Density | M | ASTM D 792 | 1.17 | g/cm³ |
Tensile strength | E | ASTM D 412 | 3000 | psi |
Elongation @ break | E | ASTM D 412 | 560 | % |
Tensile stress @ 50% elongation | E | ASTM D 412 | 410 | psi |
Tensile stress @ 100% elongation | E | ASTM D 412 | 470 | psi |
Tensile stress @ 300% elongation | E | ASTM D 412 | 990 | psi |
Tear strength | E | ASTM D 624 | 320 | pli |
Flexural modulus @ 23°C | M | ASTM D 790 | 2020 | psi |
Flexural modulus @ -29°C | M | ASTM D 790 | 7480 | psi |
Taber abrasion H-18 wheel 1000g | M | ASTM D 3389 | 15 | mg/1000 cycles |
Bayshore rebound resilience | M | ASTM D 2632 | 45 | % |
Compression set at 22h @ 23°C | M | ASTM D 395 | 34 | % |
Compression set at 22h @ 70°C | M | ASTM D 395 | 94 | % |
Softening range low | E | Huntsman TMA | 112 | °C |
Softening range high | E | Huntsman TMA | 131 | °C |
Glass transition temperature (DSC) | E | ASTM D 3418 | -31 | °C |
Vicat softening point VST/A120 | M | ASTM D 1525 | 52 | °C |
M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.