IROGRAN® A 90 P 5055 FCM

Polyether-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 90 P 5055 FCM is a food contact approved polyether-based Thermoplastic Polyurethane (TPU) for melt calendering. Key features are excellent hydrolysis and microbial resistance and excellent wear performance.

MAIN APPLICATIONS:

Thin wall extrusion profiles and calendering applications.

Details

25.07.2019FW - Remove DP and update of the physical properties

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ISO 7619	88	Shore A
Hardness (after 3 sec.)	M	ISO 7619	34	Shore D
Density	M	ISO 1183-1	1,12	g/cm³
Tensile strength	M	DIN 53504	30	MPa
Elongation @ break		DIN 53504	600	%
Tensile stress @ 100% elongation	M	DIN 53504	7,0	MPa
Tensile stress @ 300% elongation	M	DIN 53504	11	MPa
Tear strength	M	ISO 34-1	60	N/mm
Abrasion	M	ISO 4649	35	mm³
Bayshore rebound resilience	M	ASTM D 2632	36	%
Compression set at 70h @ 23°C	M	ISO 815	25	%
Compression set at 24h @ 70°C	M	ISO 815	45	%
Mold shrinkage	M	ISO 294-4	0,9	%
Softening range low	E	Huntsman TMA	150	°C
Softening range high	E	Huntsman TMA	170	°C

M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 10kg] ISO 1133-1 = 90 cm³/10min

Processing Parameter:	Extrusion
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	165 - 190
Die Head:	180 - 190
Nozzle:	180 - 200
Processing Parameter:	Calendering
Temperature Profile	°C
Front Roll:	160 - 180
Rear Roll:	160 - 180

View Pdf-File