IROGRAN® A 70 H 4714N

Polyester-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 70 H 4714N is a polyester-based Thermoplastic Polyurethane (TPU) for injection molding applications. Key features are phthalate-free, low hardness and modulus, excellent wear performance, good low temperature performance, high elasticity and high transparency.

MAIN APPLICATIONS:

Thick wall technical parts and thin wall technical parts.

Details

At Jan.2016: US / EAIME / APAC - / MTO / MTO finished 08.10.2016

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ISO 7619	73	Shore A
Hardness (after 3 sec.)	M	ISO 7619	24	Shore D
Density	M	ISO 1183-1	1,18	g/cm³
Tensile strength	M	DIN 53504	43	MPa
Elongation @ break	M	DIN 53504	650	%
Tensile stress @ 100% elongation	M	DIN 53504	3,4	MPa
Tensile stress @ 300% elongation	M	DIN 53504	9,0	MPa
Tear strength	M	ISO 34-1	63	N/mm
Abrasion	M	ISO 4649	30	mm³
Bayshore rebound resilience	M	ASTM D 2632	52	%
Compression set at 70h @ 23°C	M	ISO 815	25	%
Compression set at 24h @ 70°C	M	ISO 815	36	%
Mold shrinkage	M	ISO 294-4	2,7	%
Softening range low	E	Huntsman TMA	150	°C
Softening range high	E	Huntsman TMA	165	°C

M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 5kg] ISO 1133-1 = 15 cm³/10min

Processing Parameter:	Injection Molding
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	175 - 180
Nozzle:	175 - 190
Mold:	20 - 50