IROGRAN® A 70 H 4714N

Polyester-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 70 H 4714N is a polyester-based Thermoplastic Polyurethane (TPU) for injection molding applications. Key features are phthalate-free, low hardness and modulus, excellent wear performance, good low temperature performance, high elasticity and high transparency.

MAIN APPLICATIONS:

Thick wall technical parts and thin wall technical parts.

Details

At Jan.2016: US / EAIME / APAC - / MTO / MTO finished 08.10.2016

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ASTM D 2240	73	Shore A
Hardness (after 3 sec.)	M	ASTM D 2240	24	Shore D
Density	M	ASTM D 792	1.18	g/cm³
Tensile strength	M	ASTM D 412	5510	psi
Elongation @ break	M	ASTM D 412	800	%
Tensile stress @ 100% elongation	M	ASTM D 412	570	psi
Tensile stress @ 300% elongation	M	ASTM D 412	1300	psi
Tear strength	M	ASTM D 624	495	pli
Abrasion	M	ISO 4649	30	mm³
Bayshore rebound resilience	M	ASTM D 2632	52	%
Compression set at 70h @ 23°C	M	ASTM D 395	25	%
Compression set at 24h @ 70°C	M	ASTM D 395	36	%
Mold shrinkage	M	ASTM D 955	2.7	%
Softening range low	E	Huntsman TMA	150	°C
Softening range high	E	Huntsman TMA	165	°C

M = Injection moulded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 5kg] ISO 1133-1 = 15 cm³/10min

Processing Parameter:	Injection Molding
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	175 - 180
Nozzle:	175 - 190
Mold:	20 - 50

View Pdf-File