IROGRAN® A 85 C 4002

Polycaprolactone-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 85 C 4002 is a polycaprolactone-based Thermoplastic Polyurethane (TPU) for injection molding applications. Key features are good oil and solvent resistance, low compression set, excellent wear performance and short cycle times.

MAIN APPLICATIONS:

Thick wall technical parts and seals and gaskets.

Details

At Jan.2016: US / EAIME / APAC - / MTS / MTO finished 08.10.2016

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ISO 7619	85	Shore A
Hardness (after 3 sec.)	M	ISO 7619	35	Shore D
Density	M	ISO 1183-1	1,18	g/cm³
Tensile strength	M	DIN 53504	55	MPa
Elongation @ break	M	DIN 53504	560	%
Tensile stress @ 100% elongation	M	DIN 53504	3,5	MPa
Tensile stress @ 300% elongation	M	DIN 53504	9,0	MPa
Tear strength	M	ISO 34-1	50	N/mm
Abrasion	M	ISO 4649	35	mm³
Compression set at 70h @ 23°C	M	ISO 815	30	%
Compression set at 24h @ 70°C	M	ISO 815	38	%
Mold shrinkage	M	ISO 294-4	0,8	%
Softening range low	M	Huntsman TMA	175	°C
Softening range high	M	Huntsman TMA	185	°C

M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing

Processing Parameters

Melt Volume Rate [190°C / 21,6kg] ISO 1133-1 = 5 cm³/10min

Processing Parameter:	Injection Molding
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	195 - 210
Nozzle:	195 - 210
Mold:	20 - 50

View Pdf-File