IROGRAN® A 85 C 4957

Polyester-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 85 C 4957 is a polyester-based Thermoplastic Polyurethane (TPU) for extrusion and injection molding applications. Key features are excellent wear performance and good low temperature performance.

MAIN APPLICATIONS:

Thin wall extrusion profiles and spiral hoses.

Details

At Jan.2016: US / EAIME / APAC - / MTO / MTS finished 08.10.2016

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ISO 7619	85	Shore A
Hardness (after 3 sec.)	M	ISO 7619	34	Shore D
Density	M	ISO 1183-1	1,22	g/cm³
Tensile strength	M	DIN 53504	40	MPa
Elongation @ break	M	DIN 53504	700	%
Tensile stress @ 100% elongation	M	DIN 53504	5,8	MPa
Tensile stress @ 300% elongation	M	DIN 53504	9,7	MPa
Tear strength	M	ISO 34-1	70	N/mm
Abrasion	M	ISO 4649	30	mm³
Bayshore rebound resilience	M	ASTM D 2632	36	%
Compression set at 70h @ 23°C	M	ISO 815	18	%
Compression set at 24h @ 70°C	M	ISO 815	40	%
Mold shrinkage	M	ISO 294-4	1,0	%
Softening range low	E	Huntsman TMA	155	°C
Softening range high	E	Huntsman TMA	165	°C

M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [195°C / 8,7kg] ISO 1133-1 = 30 cm³/10min

Processing Parameter:	Extrusion
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	190 - 210
Die Head:	190 - 210
Nozzle:	190 - 210

View Pdf-File