Polyester-based Thermoplastic Polyurethane
| Properties | Key | NORM | Value | Unit |
|---|---|---|---|---|
| Hardness (after 3 sec.) | M | ASTM D 2240 | 87 | Shore A |
| Hardness (after 3 sec.) | M | ASTM D 2240 | 43 | Shore D |
| Density | M | ASTM D 792 | 1.20 | g/cm³ |
| Tensile strength | E | ASTM D 412 | 6960 | psi |
| Elongation @ break | E | ASTM D 412 | 570 | % |
| Tensile stress @ 50% elongation | E | ASTM D 412 | 780 | psi |
| Tensile stress @ 100% elongation | E | ASTM D 412 | 890 | psi |
| Tensile stress @ 300% elongation | E | ASTM D 412 | 1710 | psi |
| Tear strength | E | ASTM D 624 | 470 | pli |
| Flexural modulus @ 23°C | M | ASTM D 790 | 4850 | psi |
| Flexural modulus @ -29°C | M | ASTM D 790 | 43570 | psi |
| Abrasion | M | ISO 4649 | 30 | mm³ |
| Taber abrasion H-18 wheel 1000g | M | ASTM D 3389 | 22 | mg/1000 cycles |
| Bayshore rebound resilience | M | ASTM D 2632 | 31 | % |
| Compression set at 22h @ 23°C | M | ASTM D 395 | 37 | % |
| Compression set at 22h @ 70°C | M | ASTM D 395 | 88 | % |
| Mold shrinkage | M | ASTM D 955 | 1.2 | % |
| Softening range low | E | Huntsman TMA | 146 | °C |
| Softening range high | E | Huntsman TMA | 160 | °C |
| Glass transition temperature (DSC) | E | ASTM D 3418 | -27 | °C |
| Vicat softening point VST/A120 | M | ASTM D 1525 | 74 | °C |
M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.
Melt Volume Rate [190°C / 10kg] ISO 1133-1 = 60 cm³/10min
| Processing Parameter: | Extrusion |
| Temperature Profile | °C |
| Feed Zone: | 25 - 40 |
| Barrel: | 170 - 195 |
| Die Head: | 175 - 200 |
| Nozzle: | 175 - 200 |
| Processing Parameter: | Calendering |
| Temperature Profile | °C |
| Front Roll: | 160 - 180 |
| Rear Roll: | 160 - 180 |